Active agent T11 is an additive specifically used in addition molded silicone rubber, which can improve system operability, harden more efficiently, and reduce costs. The main component of T11 is a composite of long-chain silane, which meets all environmental RoHS requirements and can be safely used in any addition silicone system.

become   Divided:Long bond alkyl silane mixture
volatility:2—4%
Yan   Color:Transparent slightly yellow
sticky   Degree:Below 10cps

T11 additive usage:

explain
· The hardening process of additive silicone typically involves three stages: initiation, gelation, and termination.
· When using platinum complexes in small amounts, the gelation period is usually long, and increasing the amount can lead to a shorter initiation period. At this point, it is difficult to achieve ideal results using either ethylene double capped agents or alkynes as delay agents.
· The use of active agent T11 can effectively solve this problem by prolonging the initiation period and shortening the gelation period,
· The activator T1 can only activate platinum complexes and cannot replace platinum complexes.
· Both room temperature hardening systems, high-temperature hardening systems, and extrusion systems can be used.

use
· It can be pre mixed separately with agent A (on the side of active platinum), or pre mixed separately with agent B (on the side of hydrogen containing silicone oil). It can also be added together during use (when A and B agents are mixed).
· If pre mixed with platinum complex alone, the platinum content needs to be diluted first, otherwise premature activation and failure will occur.
· a. The amount of addition varies depending on actual needs, usually adding 0.05-0.20% to the total weight.
b. The amount of platinum complex added can be reduced by 5-20%.
c. A system that calculates processes in seconds at high temperatures can reduce processes by 20-50%.
· Users of homemade platinum complexes do not need to add vinyl monomers or alkyne based retardants after using T11.
· Excessive addition may cause slight yellowing, resulting in a slight touch on the surface in contact with air in the room temperature hardening system.