Polyethylene oxide PEO resin PEO-3Z polyethylene oxide is used in industrial fields such as coatings, inks, batteries, and electric light sources. It is used as a non-ionic thickener in water-based wood coatings, with an added amount of 0.5% -1%; In fluorescent lamps, it serves as a binder for fluorescent powder, with uniform powder coating, good adhesion to the wall, minimal residue after baking, and long lifespan; Applied in cosmetics, thickening and thixotropic agent, good hand feel, SUMITOMO CHEMICAL

• Describe
• Specifications
• Application
• Service

SUMITOMO CHEMICAL PEO-3Z polyethylene oxide is a non-ionic water-soluble resin. Overview:

PEO-3Z PEO polyethylene oxide is a non-ionic water-soluble resin, which is a high molecular weight white powder.

PEO-3Z PEO polyethylene oxide molecular weight ranges from 600000 to 1.1 million, and at 25 ℃, the viscosity of a 5% PEO-3Z aqueous solution is between 2500-5500mpa. s 

Characteristics of PEO-3Z PEO polyethylene oxide:

        · Completely water-soluble

        · Dissolve in many solvents

        · PEO is a non-ionic polymer

        · Efficient thickening (even with high viscosity at very low concentrations)

        · Due to being a thermoplastic resin, it has excellent ductility, plasticity, and bending properties

        · Prevent biological invasion

        · Reduce the friction of liquids

        · Can be combined with various polar resins such as urea based resin, acrylic acid, furan resin, etc

        · Low toxicity 

SUMITOMO CHEMICAL PEO-3Z polyethylene oxide is a non-ionic water-soluble resin packaging specification:

SUMITOMO CHEMICAL PEO-3Z polyethylene oxide is a non-ionic water-soluble resin. Its applications include:

Although PEO resin is completely water-soluble, the key to preparing an aqueous solution is how to completely disperse PEO powder in water. A simple method is to gradually add PEO to water at an appropriate stirring speed (1-1.5m/s). The prepared adhesive solution is transparent and clear, and there is no impurity precipitation after placement. 

PEO-3Z PEO polyethylene oxideIt should be noted that:

· PEO is a high molecular weight resin, and high-speed stirring can break its molecular chains, reducing the viscosity of the adhesive. Therefore, the stirring speed should be controlled.

 · PEO aqueous solution is prone to decomposition when exposed to light (especially ultraviolet light), so the prepared powder should be covered and stored in a cool place.

 · The viscosity of PEO aqueous solution is greatly affected by temperature, and the viscosity decreases with increasing temperature. When preparing, it is important to maintain a stable ambient temperature as much as possible.

After sales service commitment · Enjoy worry free procurement

Operating for 20 years

Integrity first, unchanged original intention: to be an explorer and guide in the industry

Quality assurance

International renowned chemical brand's general agent in China, all products are genuine and licensed

Worry free procurement

Any dissatisfaction can be returned or exchanged within 15 days

Inventory Guarantee

Multiple large professional warehouses with sufficient inventory reserves to prevent shortages and price increases

Lightning delivery

Same day shipping, free delivery within 48 hours to surrounding areas

technical guidance

Master of Chemistry, 20-year Chemical Application Practice Team, providing technical guidance